PRIMID TP 105 

FOR POWDER COATINGS
 
 
Chemical name N,N,N',N'-Tetrakis (2-hydroxyethyl) adipamide 
Appearance 
Colour Gardner ISO4630white, crystalline solid 
< 1
Melting Point 
Water Content120 - 124 °C 
< 1%
Hydroxy equivalent weight 82+-2
Mixing ratio 95:5 

 
TP 105 is an alkylamine crosslinker with –OH functionality capable to crosslink carboxyl functional polyester for highly exterior durable powder coatings applications.
 
ORIENTATIVE FORMULATION (PES/TP105 95:5)
 
                                                 (parts by weight)  
  Polyester  resin                                 56,0
  TP 105                                             3,0
  Kronos 2310 (TiO2)                         40,0
  Thixatrol ST                                          0,8
  Benzoin                                               0,2 
 
Gel time: 200ºC – 90”
Curing requirement：200℃   8 minutes
 
POLYESTER type (From China):
  Appearance：                          pale yellow flake
  Acid number:                           30±5mgKOH/g
  Viscosity at 175ºC                   3,5---6,0  Pa·S
  Softening point:                 95----110℃
  Glass transition（DSC）：      >50℃
 
 
 
 
 
 
 
Basic properties of coating film（film thickness 60μm） 
  Impact（direct.reverse）     50Kg·cm
  Pencil hardness             H
  Bending（ф2mm）         pass
  Gloss（60°）             >90%
  QUVB313 240             ≥75%
 
 
Application:
Mainly used as Curing Agent for polyester powder coating. It imparts good weather stability due to its very stable chemical nature. It provides good reactivity through its free functional hydroxyl groups when it is combined with resins containing carboxyl groups as saturated polyesters. The powder will cure with no emision of VOC.
 
Packing:
In bags of 20kgs net each with plastic lining.
 
Claim: above information is offered as a recommendation only